Composite panel having subsonic transverse wave speed characteristics

ABSTRACT

A composite panel has first and second sheets sandwiching a core with at least one of the sheets being attached to the core at first regions thereof and unattached to the core at second regions thereof.

ORIGIN OF THE INVENTION

The invention described herein was made by employees of the United States Government and may be manufactured and used by or for the Government for governmental purposes without the payment of any royalties thereon or therefor.

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention relates to composite panels. More specifically, the invention is a composite panel that has subsonic transverse wave speed characteristics in regions thereof for reduced sound radiation efficiency and increased sound power transmission loss.

2. Description of the Related Art

Composite materials are used in many construction applications (e.g., structures, aircraft, trains, vehicles, industrial machines, etc.) because of their light weight and strength. The materials are frequently formed into what are known as composite panels where two sheets of one type of material are sandwiched about another type of core material. For example, one type of composite panel has two sheets of a material such as graphite-epoxy, epoxy, fiberglass or aluminum sandwiched about a honeycomb core made from materials such as NOMEX, aluminum or paper. The resulting composite panel is light and stiffer than any of its component parts. However, as can be the case with most lightweight and stiff materials, sound can be radiated very efficiently because the transverse wave speed through the panel can be greater than the speed of sound in air. In other words, the composite panel has a supersonic transverse wave speed. If the composite panel is to be used to define a human-occupied interior space, noise radiated by the composite panel into the interior space may be unacceptable. Current methods of addressing this noise problem have involved the addition of noise control material to the composite panel such that the noise-controlled composite panel is characterized by a subsonic transverse wave speed. Suggested additions include a limp mass (e.g., lead vinyl) applied to one or both of the composite panel's face sheets and/or the inclusion of foam within the composite panel's core in the case of a honeycomb core. However, the extra noise-control material adds cost and weight to the composite panel.

SUMMARY OF THE INVENTION

Accordingly, it is an object of the present invention to provide a composite panel having subsonic transverse wave speed characteristics.

Another object of the present invention is to provide a composite panel that does not require the addition of noise control material to achieve subsonic transverse wave speed characteristics.

In accordance with the present invention, a composite panel has first and second sheets sandwiching a core. At least one of the first and second sheets is attached to the core at first regions thereof and unattached to the core at second regions thereof.

BRIEF DESCRIPTION OF THE DRAWINGS

Other objects, features and advantages of the present invention will become apparent upon reference to the following description of the preferred embodiments and to the drawings, wherein corresponding reference characters indicate corresponding parts throughout the several views of the drawings and wherein:

FIG. 1 is an exploded perspective view of a composite panel having a core with recessed regions in accordance with an embodiment of the present invention;

FIG. 2 is a cross-sectional view of the composite panel of FIG. 1 in its assembled form;

FIG. 3 is a cross-sectional view of a composite panel in accordance with another embodiment of the present invention where the recesses are different sizes;

FIG. 4 is a cross-sectional view of a composite panel in accordance with another embodiment of the present invention where the recesses are formed on either side of the core in a mirror-image fashion;

FIG. 5 is a cross-sectional view of a composite panel in accordance with another embodiment of the present invention where the recesses are formed on either side of the core in a non-mirror-image fashion;

FIG. 6 is a cross-sectional view of a composite panel in accordance with another embodiment of the present invention where areas of non-attachment are provided between the core and face sheets;

FIG. 7 is a cross-sectional view of the composite panel of FIG. 2 further having acoustically absorbent material in the panel's recesses; and

FIG. 8 is a cross-sectional view of a composite panel in accordance with another embodiment of the present invention where recesses are formed in one of the face sheets.

DETAILED DESCRIPTION OF THE INVENTION

Referring now to the drawings, and more particularly to FIGS. 1 and 2, a composite panel in accordance with an embodiment of the present invention is shown and is referenced generally by numeral 10. For illustration, composite panel 10 is a flat panel. However it is to be understood that composite panels constructed in accordance with the present invention can also be shaped to define contoured panels as needed.

Composite panel 10 has face sheets 12 and 14 sandwiched about a core 16. Face sheets 12 and 14 can be the same or different materials. Suitable materials for face sheets 12 and 14 include, but are not limited to, graphite epoxy, aluminum and fiberglass. Core 16 is a lightweight material that is bonded, attached or adhered (in ways well understood in the art) to face sheets 12 and 14 to form composite panel 10 such that the stiffness of composite panel 10 is greater than the stiffness of it's component parts. As a result, while the transverse wave speed for typical materials and thicknesses of face sheets 12 and 14 is subsonic, the transverse wave speed is very often supersonic for a composite panel using these face sheets. Suitable constructions for core 16 include, but are not limited to, a honeycomb structure, a truss structure, or a foam structure. Suitable materials for core 16 include, but are not limited to, NOMEX, paper and aluminum in the case of honeycomb cores, and polymers and carbon in the case of foam cores. The core can be of varying thicknesses depending, for example, on a particular application, without departing from the scope of the present invention.

One embodiment of the present invention addresses this problem by forming recesses in core 16 adjacent face sheet 12. More specifically, an array of recesses 18 are formed in core 16 so that face sheet 12 is only bonded/attached/adhered to core 16 at regions 16A while the entire side of face sheet 14 is bonded/attached/adhered to the other side of core 16 as indicated by 14A. The number, size, depth and shape of recesses 18 and resulting size/shape of regions 16A can vary without departing from the scope of the present invention. In general, a balance must be struck between stiffness requirements and noise requirements of composite panel 10. With respect to noise reduction, the greater the area of the recesses, the greater the reduction in sound radiation efficiency and increase in sound power transmission loss. This is because each region 12A of face sheet 12 adjacent to a recess 18 is uncoupled from core 16 so that transverse wave speed at this local region of composite panel 10 is reduced to the subsonic transverse wave speed of face sheet 12. With respect to stiffness, composite panel 10 must have sufficient attachment regions 16A (between face sheet 12 and core 16) to achieve the necessary stiffness requirements. Accordingly, any given application of the present invention will require these two criteria to be balanced.

In the illustrated embodiment discussed thus far, identically-sized recesses 18 are formed just on one side of core 16. However, the present invention is not so limited. For example, composite panel 30 in FIG. 3 has recesses 38 formed in core 16 that are of different sizes. Note that the shapes of recesses 38 could vary too. In FIG. 4, composite panel 40 has recesses 48 formed on either side of core 16 in a mirror-image fashion so that the regions of face sheets 12 and 14 contacting and attached to core 16 are similarly mirror images of one another. Composite panel 50 in FIG. 5 utilizes recesses 58 on opposing sides of core 16, but in a non-mirror-image fashion.

Another embodiment of the present invention is illustrated by a composite panel 60 in FIG. 6 where, rather than forming recesses in core 16, regions of non-attachment 16B are formed between face sheets 12/14 and core 16. That is, face sheets 12 and 14 are coupled to core 16 only at attachment regions 16A while remaining uncoupled or unattached to core 16 at non-attached regions 16B. As sound radiates through composite panel 60, friction losses will be generated between the non-attached regions 16B of core 16 and face sheets 12 and 14. In many applications, this will be sufficient to produce a satisfactory low frequency response. However, higher-frequency buzzing may occur thereby making this embodiment most suitable for applications where high-frequency buzzing is not problematic.

Still another embodiment of the present invention involves adding an acoustically absorbent material (a wide variety of which are well known in the art) to some or all of the recesses formed in the composite panel's core. For example, FIG. 7 illustrates the FIG. 2 embodiment with recesses 18 further having an acoustically absorbent material 20 partially or completely filling recesses 18.

The present invention is not limited to the formation of recesses in the core of a composite panel. For example, a composite panel 70 illustrated in FIG. 8 has recesses 78 formed in face sheet 12. Although not illustrated, recesses could also be formed in face sheet 14 in a mirror-image or non-mirror-image fashion with respect to recesses 78. Still further, recesses could be formed in one or both of face sheets 12/14 and in core 16 without departing from the scope of the present invention.

The advantages of the present invention are numerous. Composite panels having local regions characterized by subsonic transverse wave speeds can be constructed without requiring the addition of noise control material. Rather, the present invention addresses the transverse wave speed problem of composite panels by actually eliminating material thereby decreasing the weight of the panel. Cores and/or face sheets with recesses formed therein can be easily achieved using automated manufacturing processes. The present invention can be used wherever composite materials are used in weight sensitive, noise environments such as aerospace and ground vehicles, trains and industrial machines.

Although only a few exemplary embodiments of this invention have been described in detail above, those skilled in the art will readily appreciate that many modifications are possible in the exemplary embodiments without materially departing from the novel teachings and advantages of this invention. Accordingly, all such modifications are intended to be included within the scope of this invention as defined in the following claims. In the claims, means-plus-function and step-plus-function clauses are intended to cover the structures or acts described herein as performing the recited function and not only structural equivalents, but also equivalent structures. Thus, although a nail and a screw may not be structural equivalents in that a nail employs a cylindrical surface to secure wooden parts together, whereas a screw employs a helical surface, in the environment of fastening wooden parts, a nail and a screw may be equivalent structures. 

1. A composite panel comprising first and second sheets sandwiching a core with at least one of said first and second sheets attached to said core at first regions thereof and unattached to said core at second regions thereof.
 2. A composite panel as in claim 1 wherein each of said second regions is a recess formed in at least one of said core, said first sheet and said second sheet.
 3. A composite panel as in claim 1 wherein said first and second sheets are the same material.
 4. A composite panel as in claim 1 wherein said first and second sheets are different materials.
 5. A composite panel as in claim 1 wherein said core is selected from the group consisting of a honeycomb core, a truss core and a foam core.
 6. A composite panel as in claim 1 wherein transverse wave speed of each of said first and second sheets is subsonic.
 7. A composite panel as in claim 1 wherein said second regions adjacent to said first sheet are mirror imaged with respect to said second regions adjacent to said second sheet.
 8. A composite panel as in claim 1 wherein said second regions are identically sized and shaped.
 9. A composite panel as in claim 2 further comprising acoustically absorbent material in said recess.
 10. A composite panel comprising first and second sheets adjacent to and sandwiching a core therebetween with at least one of said first and second sheets attached to said core at first regions thereof and unattached to said core at second regions thereof such that said composite panel is characterized as having a subsonic transverse wave speed at portions thereof bounded by said second regions.
 11. A composite panel as in claim 10 wherein each of said second regions is a recess formed in at least one of said core, said first sheet and said second sheet.
 12. A composite panel as in claim 10 wherein said first and second sheets are the same material.
 13. A composite panel as in claim 10 wherein said first and second sheets are different materials.
 14. A composite panel as in claim 10 wherein said core is selected from the group consisting of a honeycomb core, a truss core and a foam core.
 15. A composite panel as in claim 10 wherein transverse wave speed of each of said first and second sheets is subsonic.
 16. A composite panel as in claim 10 wherein said second regions adjacent to said first sheet are mirror imaged with respect to said second regions adjacent to said second sheet.
 17. A composite panel as in claim 10 wherein said second regions are identically sized and shaped.
 18. A composite panel as in claim 11 further comprising acoustically absorbent material in said recess.
 19. A composite panel as in claim 10 wherein a face of said first sheet is completely attached to said core.
 20. A composite panel as in claim 19 wherein each of said second regions is a recess formed in at least one of said core and said second sheet.
 21. A composite panel as in claim 19 wherein said core is selected from the group consisting of a honeycomb core, a truss core and a foam core.
 22. A composite panel as in claim 19 wherein said second regions are identically sized and shaped. 